Effect on microstructure and hardness of 1 MeV carbon ion implantation in Al, Co and W

Carbon implantation is used to change the surface properties of materials without changing the bulk properties in various fields such as microelectronics, optics, tribology and biomaterials. While this implantation is usually performed at energies lower than 200 key and thus in the low energy range of the stopping power curve, here we studied the effect of a I MeV ion beam which is in the medium energy range. The higher energies increase the modified depth range and thereby the load-carrying ability of metal surfaces. Light (Al), medium (Co) and heavy (W) metals were chosen as substrates. Three ion fluencies of 10(16) ions/cm(2), 10(17) ions/cm(2), and 10(18) ions/cm2 were used. Nuclear reaction analysis evidenced the presence of carbon at the samples surface and at a depth in accordance with Monte-Carlo (SRIM) simulations. Glancing incidence X-ray diffraction (GIXRD) allowed us to reveal the formation of aluminum carbide while no carbide was observed for Co and W. The modifications of the lattice parameters of Co and of W were studied by Rietveld refinements of X-ray diffraction patterns. For these metals the increase of the profile asymmetry of the diffraction peaks can result from the generation of dislocations induced by irradiation. The hardness measured by nano-indentation tests increases with the carbon ion dose, and the rise of hardness is larger for aluminum and tungsten than for cobalt. (C) 2015 Elsevier B.V. All rights reserved.